TiC based cermet rod
Techinical Data
Langfeng Metallic’s product standard
| Commodity: TITANIUM CARBIDE CERMET RODS | |||||||||||||
| Grade: LFT12 | |||||||||||||
| PHYSICAL | CHEMICAL | ||||||||||||
| Compositions | wt.% | ||||||||||||
| TRS（ISO 3327） | 1800 +200 N/mm2 | Ni | 2.0 | ||||||||||
| Hardness（ISO 3878） | 82.5±0.5 HRA | TiC | 47.0 | ||||||||||
| Density（ISO 3369） | 6.2 ±0.2 g/cm3 | Fe | 37.0 | ||||||||||
| Average Grain Size | 2.0 ±0.5 μm | Mn | 10.0 | ||||||||||
| Porosities | A02B00C00 | Other | 4.0 | ||||||||||
Product introduction
The main technical indicators:
1. Hardness: 82-89 HRA
2. The density: 6.0 to 6.5 g/cm3;
Products are mainly applied to the alloy ball, hammer head, alloy plate and large crusher hammers, large ball mill wearing parts, improve the service life of equipment;
The main characteristic of the product: high temperature corrosion resistance, wear resistance;
Wear parts for the processing of TIC rods considerations:
1) steel is suitable for the high manganese steel material.
2) steel casting than normal without the improvement of TIC 60-100 degrees,
3)before make and fly a TIC rod boron salt water soaking liquid, remove dry and then use (DNA)
4) casting, fixed first TIC on steel, JiaoGangShui again, (because the density of TIC is lighter than steel,
Without fixed first TIC rods, stick instability.
5) after forming, heat treatment, and water toughening treatment with high manganese steel water
1. Hardness: 82-89 HRA
2. The density: 6.0 to 6.5 g/cm3;
Products are mainly applied to the alloy ball, hammer head, alloy plate and large crusher hammers, large ball mill wearing parts, improve the service life of equipment;
The main characteristic of the product: high temperature corrosion resistance, wear resistance;
Wear parts for the processing of TIC rods considerations:
1) steel is suitable for the high manganese steel material.
2) steel casting than normal without the improvement of TIC 60-100 degrees,
3)before make and fly a TIC rod boron salt water soaking liquid, remove dry and then use (DNA)
4) casting, fixed first TIC on steel, JiaoGangShui again, (because the density of TIC is lighter than steel,
Without fixed first TIC rods, stick instability.
5) after forming, heat treatment, and water toughening treatment with high manganese steel water